OLA

Mechanical Properties

Density (20°C, g/cm³): 2.82 Elongation (1.6 mm / 1/16 in thickness): 11% Tensile Strength (25°C, MPa): 572 Yield Strength (25°C, MPa): 503 Hardness (500 kgf, 10 mm ball): 150 Modulus of Elasticity (GPa): 71

Thermal Properties

Melting Range (°C): 475–635 Coefficient of Thermal Expansion (20–100°C, μm/m·K): 23.6

Electrical Properties

Electrical Conductivity (20°C / 68°F, % IACS): 33 Electrical Resistivity (20°C / 68°F, mm²/m): 0.0515

Mechanical Properties

Density (20°C, g/cm³): 2.73 Tensile Strength (25°C, MPa): 290 Yield Strength (25°C, MPa): 240 Modulus of Elasticity (GPa): 71 Elongation (1.6 mm / 1/16 in thickness): 12% Hardness (500 kgf, 10 mm ball): 95

Electrical Properties

Electrical Conductivity (20°C / 68°F, % IACS): 43 Electrical Resistivity (20°C / 68°F, Ω·mm²/m): 0.040